clause5.io/ welding/ weld-defects/ Perforación por quemado-Soldadura
Burn-Through Weld — Causas, Prevención & D1.1:2025 Repair
Burn-through occurs when excessive Aporte Térmico melts completely through the Metal Base. Under D1.1:2025 Clause 7.23, burn-through is a Perfil de soldadura Defecto requiring Reparación. Repair procedure is governed by Clause 7.25.1 — remove to sound metal, re-weld per approved WPS, re-inspect.
What Is Burn-Through
Burn-through is a weld defect where excessive heat input melts completely through the base metal, creating a hole or severe depression in the weld zone. Unlike Porosidad or Socavado which affect the weld cross-section, burn-through penetrates through the base material itself.
Under D1.1:2025, burn-through is classified as a weld profile defect under Clause 7.23, not separately named in Tabla 8.1 as a Discontinuidad Categoría. It is evaluated as a weld profile nonconformance. When burn-through creates a hole or severe profile violation, it fails Inspección Visual under Clause 8.9 and requires repair.
D1.1:2025 Clause 7.23 — Weld Profile Requirements
Clause 7.23 governs the visual appearance and profile of completed welds. Soldadura de Filete profiles must meet Figure 7.4 Requisitos. Soldadura de ranura faces shall be A ras or have reinforcement within specified Límites.
Burn-through creates a profile defect that fails visual Inspección under Clause 8.9 when it results in an incomplete weld profile or penetration through the base metal. The defect may also create stress concentrations detrimental to structural performance. Because the base metal itself is compromised, burn-through cannot be corrected by simply adding more Metal de Soldadura — the repair procedure under Clause 7.25.1 must be followed.
Causes of Burn-Through
Four primary causes drive burn-through failures:
Excessive heat input — Amperaje set too high for the material Espesor generates more heat than the base metal can conduct away. The weld pool grows beyond the Geometría de la junta and melts through.
Wrong travel speed — Moving the Electrodo too slowly concentrates heat in one location. Even at correct amperage, insufficient Velocidad de Avance can cause cumulative heat buildup that results in burn-through, particularly on thinner sections.
Thin base metal — Material that is too thin for the Proceso de Soldadura parameters cannot dissipate heat fast enough. The same parameters that weld heavier plate without issue will burn through thin material.
Incorrect electrode diameter — An oversized electrode deposits more heat than the joint requires. Matching Diámetro del electrodo to the material thickness and joint configuration is a fundamental WPS parameter that directly controls burn-through risk.
Prevention
Effective prevention requires matching all heat input parameters to the material thickness as specified in the WPS. Verificar amperage, Voltaje, and travel speed settings before production Soldadura. Use the smallest electrode diameter appropriate for the joint configuration. On thin material, stay at the low end of the WPS amperage range.
For thin base metal, intermittent Técnica de soldadura — depositing short weld segments and allowing each to cool — limits cumulative heat accumulation. A copper Barra de respaldo behind the joint provides a heat sink and reduces burn-through risk when the joint configuration permits its use.
WPS parameter check: Before welding thin material, verify that the electrode diameter specified in the WPS is appropriate for the joint thickness. An electrode diameter change that exceeds the Variable esencial limits in Table 6.6 requires a new WPS qualification — not just a parameter adjustment.
Repair per Clause 7.25.1
D1.1:2025 Clause 7.25.1 governs repair of defective welds. Burn-through repair requires three steps:
Step 1 — Remove to sound metal. All defective weld metal and affected base metal must be removed back to sound material. Gouging, grinding, or machining may be used. The removed area must expose clean, unaffected base metal before re-welding begins.
Step 2 — Re-weld per approved WPS. Re-weld the area using an approved WPS appropriate for the base metal type, thickness, and joint configuration. The repair WPS must address the root cause — typically by specifying lower amperage or smaller electrode diameter than the original WPS that produced the burn-through.
Step 3 — Re-inspect. Re-inspect the repaired area using the same visual Criterios de aceptación from Table 8.1 and Clause 8.9 that identified the original defect. For CJP groove welds, complete joint penetration must be re-established and verified in the repaired area.
Frequently Asked Questions
Yes. Burn-through is a weld profile defect under D1.1:2025 Clause 7.23. It occurs when excessive heat input melts completely through the base metal, creating a hole or severe depression that fails the weld profile requirements of Clause 7.23 and visual inspection per Clause 8.9. Burn-through is not listed as a separate discontinuity category in Table 8.1 — it is evaluated as a weld profile nonconformance requiring repair.
Per D1.1:2025 Clause 7.25.1, burn-through repair requires: (1) remove the defective weld and affected base metal back to sound material; (2) re-weld the area using an approved WPS appropriate for the material type, thickness, and joint configuration; (3) re-inspect the repaired area using the same visual acceptance criteria in Table 8.1 that identified the original defect. For CJP groove welds, complete joint penetration must be re-established in the repaired area.
The four primary causes of burn-through are: (1) excessive heat input — amperage too high for the base metal thickness creates more heat than the material can conduct away; (2) insufficient travel speed — moving the electrode too slowly concentrates heat in one area; (3) thin base metal — material that is too thin for the welding process parameters cannot dissipate heat fast enough; and (4) incorrect electrode diameter — an oversized electrode deposits more heat than the joint requires. All four causes result in the weld pool melting through the base material.
Preventing burn-through on thin material requires matching process parameters to material thickness. Use the smallest electrode diameter appropriate for the joint, reduce amperage to the low end of the WPS range, increase travel speed to limit heat accumulation, and consider a heat sink (copper backing bar) behind the joint. For very thin material, intermittent welding technique — allowing each segment to cool before continuing — limits cumulative heat input. Always verify parameters on a test piece before production welding.