예열 M270M Gr.345S — H4, Low HI, ≤ 20 mm: 100°F

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

M270M Gr.345S / M270 Gr.50S의 FC 예열 이해

Shape-grade 345 MPa (50 ksi) steel for rolled bridge members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 100°F minimum preheat at ≤ 20 mm (3/4 in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345S / M270 Gr.50S이 사용되는 곳

Used as rolled W-shapes and channels in bridge cross-frames, diaphragm members, and built-up sections. The "S" shape designation indicates procurement under AASHTO M270 with shape-specific chemistry and mandatory CVN testing. Common applications include WT sections for cross-frame members, MC channels for diaphragms, and W-shapes for floor beams on shorter spans. Weld details are primarily fillet welds at gusset connections and clip angles.

M270M Gr.345S / M270 Gr.50S의 H4 수소 제어

Shape-grade Gr.345S (50S) benefits from H4 at gusset-to-shape connections where access for torch preheat is limited by flanges and stiffeners. The lower preheat achievable with H4 reduces the thermal management complexity in tight spaces typical of cross-frame subassemblies.

≤ 20 mm (3/4 in)에서 예열이 중요한 이유

Material up to 20 mm (3/4 in) covers most cross-frame angles, stiffener clips, lateral bracing members, and light bridge plate. At this thickness, hydrogen diffusion is efficient and preheat requirements are the lowest in Table 6.3 — 10°C (50°F) for both groups. In FC service, this thickness tier also carries the lowest preheat in Tables 12.4–12.7, starting at 40°C (100°F) for H4 consumables.

≤ 20 mm (3/4 in)에서의 M270M Gr.345S / M270 Gr.50S

Gr.345S (50S) shapes under 20 mm flange thickness include WT sections for K-frame cross-frames and MC channels for diaphragms. The rolled section geometry concentrates stress at the flange-to-web fillet, making proper preheat at gusset connections critical for fatigue performance. SMAW E7018 is the typical process for shape-to-plate connections in bridge subassemblies because of limited access around shape flanges.

FC 교량 용접용 H4 인증 용접재료

H4 보조 지정은 용접재료가 용착 금속 100g당 최대 4 mL의 확산성 수소를 방출함을 인증합니다. 파괴 임계 M270M Gr.345S / M270 Gr.50S에서 ≤ 20 mm (3/4 in) 두께, 1.2–2.0 kJ/mm 입열량 시 H4 용접재료는 FC 표에서 가장 낮은 예열 100°F (40°C)를 달성합니다.

H4 1.2–2.0 kJ/mm · ≤ 20 mm (3/4 in)에서의 다른 교량 강재

H4 1.2–2.0 kJ/mm에서의 M270M Gr.345S / M270 Gr.50S

다양한 조합 시도

D1.5 교량 예열 계산기를 사용하여 AASHTO M270 강재, 수소 수준 및 입열량 조합을 조회하세요. D1.1 예열 계산기도 참조하세요.