Preheat M270M Gr.345 — H4, Low HI, 20–40 mm: 150°F

M270M Gr.345 / M270 Gr.50

AASHTO M270M Gr.345 (M270 Gr.50) is the standard bridge plate and shape grade with 345 MPa (50 ksi) minimum yield, corresponding to ASTM A709 Gr.50. It is the baseline strength for modern highway bridge design per AASHTO LRFD. Used for plate girder flanges, webs, floor beams, cross-frames, and splice plates. Flanges on large plate girders routinely reach 50–75 mm (2–3 in) thick, making preheat compliance at upper thickness tiers a significant production consideration. NFC preheat per Table 6.3 Group 1; FC per Tables 12.4/12.5.

Memahami Preheat FC untuk M270M Gr.345 / M270 Gr.50

Standard 345 MPa (50 ksi) bridge plate for girders and floor beams. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 150°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Di Mana M270M Gr.345 / M270 Gr.50 Digunakan

Standard for highway bridge plate girder flanges, box girder webs, cross-frame angles, bearing sole plates, and splice plates in bolted-welded connections. Gr.345 (50) is the baseline strength for modern AASHTO LRFD bridge design. Flange butt splices, web-to-flange continuous fillet welds, and bearing stiffener clips are the dominant weld types in girder fabrication. Girder flanges typically range from 20 to 75 mm (3/4 to 3 in) thick with widths from 300 to 750 mm (12 to 30 in), requiring extended preheat soak times on thicker flange splices.

Kontrol Hidrogen H4 untuk M270M Gr.345 / M270 Gr.50

Gr.345 (50) with H4 consumables achieves the lowest FC preheat requirements available for the workhorse bridge grade. On girder fabrication lines producing 50–100 meters of flange-to-web fillet weld per shift, the reduced preheat from H4 translates directly to faster welding speed and lower fuel costs for preheat maintenance.

Mengapa Preheat Penting pada 20–40 mm (3/4–1½ in)

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

M270M Gr.345 / M270 Gr.50 pada 20–40 mm (3/4–1½ in)

At 20–40 mm, Gr.345 (50) serves splice plates, web plates, and bearing sole plates in standard highway bridge girders. CJP butt welds at flange splices are the most critical joint at this thickness — full-penetration ultrasonically-inspected joints that must pass D1.5 acceptance criteria. Preheat compliance is production-critical: 70°F minimum means heated fabrication bays in northern climates during winter bridge contracts.

Bahan Habis Pakai Bersertifikat H4 untuk Pengelasan FC Jembatan

Penunjukan tambahan H4 menyertifikasi bahwa bahan habis pakai mengendapkan tidak lebih dari 4 mL hidrogen difusibel per 100g logam yang diendapkan. Untuk fraktur kritis M270M Gr.345 / M270 Gr.50 pada ketebalan 20–40 mm (3/4–1½ in) dengan masukan panas 1.2–2.0 kJ/mm, bahan habis pakai H4 mencapai preheat terendah 150°F (70°C) di tabel FC.

Baja Jembatan Lain pada H4 1.2–2.0 kJ/mm · 20–40 mm (3/4–1½ in)

M270M Gr.345 / M270 Gr.50 pada H4 1.2–2.0 kJ/mm

Coba Kombinasi Berbeda

Gunakan Kalkulator Preheat Jembatan D1.5 untuk mencari baja AASHTO M270, tingkat hidrogen, dan kombinasi masukan panas. Lihat juga Kalkulator Preheat D1.1 untuk baja struktural.

Panduan Terkait