M270M Gr.250 पूर्वतापन — H4, Low HI, 40–60 mm: 200°F

M270M Gr.250 / M270 Gr.36

AASHTO M270M Gr.250 (M270 Gr.36) is the metric/US customary designation for the basic structural bridge steel with 250 MPa (36 ksi) minimum yield. It is the direct bridge equivalent of ASTM A709 Gr.36, procured under AASHTO M270 with mandatory Charpy V-notch testing per temperature zone. Used for secondary bridge members — lateral bracing, diaphragm plates, floor beam stiffeners, and bearing components where Gr.345 strength is not needed. Non-fracture-critical preheat follows Table 6.3 Group 1; fracture-critical follows Tables 12.4/12.5 with hydrogen and heat input as additional variables.

M270M Gr.250 / M270 Gr.36 के लिए FC पूर्वतापन को समझना

Basic 250 MPa (36 ksi) bridge steel for secondary members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 200°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.250 / M270 Gr.36 कहाँ उपयोग होता है

Specified for secondary bridge members under AASHTO LRFD — lateral bracing angles, diaphragm plates, floor beam stiffeners, bearing seat components, and railing posts. Gr.250 (36) requires CVN testing per AASHTO temperature zone, distinguishing it from plain ASTM A36 by guaranteeing fracture resistance at the bridge design service temperature. Transverse stiffener fillet welds and floor beam web-to-flange joints are high-frequency fabrication details. Temperature zones (1 through 3) determine CVN test temperature: Zone 1 at 21°C (70°F) for moderate climates, Zone 2 at 4°C (40°F) for cold, Zone 3 at -12°C (10°F) for severe cold.

M270M Gr.250 / M270 Gr.36 के लिए H4 हाइड्रोजन नियंत्रण

For Gr.250 (36), the H4 restriction to 4 mL/100g diffusible hydrogen provides the widest margin against cold cracking in secondary bridge members. The low carbon equivalent of Gr.250 already makes it one of the least crack-sensitive bridge steels, so the practical benefit of H4 over H8 is primarily preheat reduction — often 10–20°C (20–40°F) lower, which speeds production on high-volume stiffener and bracing fabrication.

40–60 mm (1½–2½ in) पर पूर्वतापन क्यों महत्वपूर्ण है

Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.

40–60 mm (1½–2½ in) पर M270M Gr.250 / M270 Gr.36

Gr.250 (36) at 40–65 mm is uncommon in modern designs because Gr.345 handles the same loads at lighter weight. When specified, it appears in bearing seats and massive foundation assemblies where material cost is secondary to simplicity. At this thickness the HAZ cooling rate is significantly slower, and the 150°F preheat reflects the need to keep cooling rates below the critical rate for hydrogen-induced cracking in the coarse-grained HAZ.

FC पुल वेल्डिंग के लिए H4-प्रमाणित उपभोज्य

H4 पूरक पदनाम प्रमाणित करता है कि उपभोज्य प्रति 100g जमा वेल्ड धातु में 4 mL से अधिक विसरणशील हाइड्रोजन जमा नहीं करता। फ्रैक्चर-क्रिटिकल M270M Gr.250 / M270 Gr.36 के लिए 40–60 mm (1½–2½ in) मोटाई पर 1.2–2.0 kJ/mm ऊष्मा इनपुट के साथ, H4 उपभोज्य FC तालिकाओं में 200°F (90°C) का सबसे कम पूर्वतापन प्राप्त करते हैं। यह पसंदीदा हाइड्रोजन स्तर है जब पूर्वतापन कमी प्राथमिकता हो।

H4 1.2–2.0 kJ/mm · 40–60 mm (1½–2½ in) पर अन्य पुल स्टील

H4 1.2–2.0 kJ/mm पर M270M Gr.250 / M270 Gr.36

विभिन्न संयोजन आज़माएँ

किसी भी AASHTO M270 स्टील, हाइड्रोजन स्तर, और ऊष्मा इनपुट संयोजन को देखने के लिए D1.5 ब्रिज पूर्वतापन कैलकुलेटर का उपयोग करें। स्ट्रक्चरल स्टील के लिए D1.1 पूर्वतापन कैलकुलेटर भी देखें।

संबंधित गाइड