Préchauffage M270M Gr.250 — H4, Low HI, ≤ 20 mm: 100°F

M270M Gr.250 / M270 Gr.36

AASHTO M270M Gr.250 (M270 Gr.36) is the metric/US customary designation for the basic structural bridge steel with 250 MPa (36 ksi) minimum yield. It is the direct bridge equivalent of ASTM A709 Gr.36, procured under AASHTO M270 with mandatory Charpy V-notch testing per temperature zone. Used for secondary bridge members — lateral bracing, diaphragm plates, floor beam stiffeners, and bearing components where Gr.345 strength is not needed. Non-fracture-critical preheat follows Table 6.3 Group 1; fracture-critical follows Tables 12.4/12.5 with hydrogen and heat input as additional variables.

Comprendre le Préchauffage FC pour M270M Gr.250 / M270 Gr.36

Basic 250 MPa (36 ksi) bridge steel for secondary members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 100°F minimum preheat at ≤ 20 mm (3/4 in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Où M270M Gr.250 / M270 Gr.36 est Utilisé

Specified for secondary bridge members under AASHTO LRFD — lateral bracing angles, diaphragm plates, floor beam stiffeners, bearing seat components, and railing posts. Gr.250 (36) requires CVN testing per AASHTO temperature zone, distinguishing it from plain ASTM A36 by guaranteeing fracture resistance at the bridge design service temperature. Transverse stiffener fillet welds and floor beam web-to-flange joints are high-frequency fabrication details. Temperature zones (1 through 3) determine CVN test temperature: Zone 1 at 21°C (70°F) for moderate climates, Zone 2 at 4°C (40°F) for cold, Zone 3 at -12°C (10°F) for severe cold.

Contrôle d'Hydrogène H4 pour M270M Gr.250 / M270 Gr.36

For Gr.250 (36), the H4 restriction to 4 mL/100g diffusible hydrogen provides the widest margin against cold cracking in secondary bridge members. The low carbon equivalent of Gr.250 already makes it one of the least crack-sensitive bridge steels, so the practical benefit of H4 over H8 is primarily preheat reduction — often 10–20°C (20–40°F) lower, which speeds production on high-volume stiffener and bracing fabrication.

Pourquoi le Préchauffage est Important à ≤ 20 mm (3/4 in)

Material up to 20 mm (3/4 in) covers most cross-frame angles, stiffener clips, lateral bracing members, and light bridge plate. At this thickness, hydrogen diffusion is efficient and preheat requirements are the lowest in Table 6.3 — 10°C (50°F) for both groups. In FC service, this thickness tier also carries the lowest preheat in Tables 12.4–12.7, starting at 40°C (100°F) for H4 consumables.

M270M Gr.250 / M270 Gr.36 à ≤ 20 mm (3/4 in)

Gr.250 (36) at up to 20 mm is the lightest bridge fabrication scenario — cross-frame angles, stiffener clips, and lateral bracing gussets. Hydrogen diffusion through this thin section is rapid, so preheat has the least influence on cracking resistance. Most fabricators use E7018 SMAW for short fillet welds at this thickness because the joint lengths are too short for mechanized FCAW setup to be economical. Interpass monitoring is minimal at this tier because heat builds slowly in thin plate.

Consommables Certifiés H4 pour Soudage FC de Ponts

Le désignateur supplémentaire H4 certifie que le consommable dépose au maximum 4 mL d'hydrogène diffusible par 100g de métal déposé. Pour fracture critique M270M Gr.250 / M270 Gr.36 à ≤ 20 mm (3/4 in) d'épaisseur avec apport de chaleur 1.2–2.0 kJ/mm, les consommables H4 atteignent le préchauffage le plus bas de 100°F (40°C) dans les tableaux FC.

Autres Aciers de Pont à H4 1.2–2.0 kJ/mm · ≤ 20 mm (3/4 in)

M270M Gr.250 / M270 Gr.36 à H4 1.2–2.0 kJ/mm

Essayez Différentes Combinaisons

Utilisez le Calculateur de Préchauffage D1.5 pour Ponts pour consulter tout acier AASHTO M270, niveau d'hydrogène et combinaison d'apport de chaleur. Voir aussi le Calculateur de Préchauffage D1.1 pour l'acier de construction.

Guides Associés