Vorwärmung M270M Gr.345W — H4, Low HI, > 60 mm: 350°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

Die FC-Vorwärmung für M270M Gr.345W / M270 Gr.50W Verstehen

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 350°F minimum preheat at > 60 mm (> 2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Wo M270M Gr.345W / M270 Gr.50W Eingesetzt Wird

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

Wasserstoffkontrolle H4 für M270M Gr.345W / M270 Gr.50W

Weathering Gr.345W (50W) with H4 benefits from reduced preheat on field splice joints where maintaining temperature in wind-exposed bridge erection conditions is challenging. The E8018-W2 low-hydrogen electrode commonly used for weathering steel field work typically carries H4 or H8 designation.

Warum Vorwärmung bei > 60 mm (> 2½ in) Wichtig ist

Material over 65 mm (2-1/2 in) includes the heaviest bridge girder flanges and box-section walls. Table 6.3 requires 110°C (225°F) for both groups at this thickness. Extended preheat soak time is necessary to achieve uniform through-thickness temperature. FC preheat for the heaviest sections reaches 180–200°C (350–400°F) at the H16 hydrogen level.

M270M Gr.345W / M270 Gr.50W bei > 60 mm (> 2½ in)

Gr.345W (50W) above 65 mm is increasingly rare as HPS345W replaces it in new designs. The conventional weathering composition at this thickness has elevated lamellar tearing risk from sulfide inclusion elongation — the problem that drove development of the HPS grades with calcium-treated, inclusion-shape-controlled steel. Existing bridges with thick 345W flanges require careful Z-direction tension checks during rehabilitation welding.

H4-Zertifizierte Zusatzwerkstoffe für FC-Brückenschweißen

Die Zusatzbezeichnung H4 zertifiziert, dass der Zusatzwerkstoff höchstens 4 mL diffusiblen Wasserstoff pro 100g abgeschiedenes Schweißgut abgibt. Für bruchkritischen M270M Gr.345W / M270 Gr.50W bei > 60 mm (> 2½ in) Dicke mit 1.2–2.0 kJ/mm Wärmeeinbringung erreichen H4-Zusatzwerkstoffe die niedrigste Vorwärmung von 350°F (180°C) in den FC-Tabellen.

Andere Brückenstähle bei H4 1.2–2.0 kJ/mm · > 60 mm (> 2½ in)

M270M Gr.345W / M270 Gr.50W bei H4 1.2–2.0 kJ/mm

Verschiedene Kombinationen Ausprobieren

Verwenden Sie den D1.5 Brücken-Vorwärmrechner für jeden AASHTO M270 Stahl, Wasserstoffniveau und Wärmeeinbringungskombination. Siehe auch den D1.1 Vorwärmrechner für Baustahl.

Verwandte Leitfäden