Vorwärmung M270M Gr.345S — H4, Low HI, 40–60 mm: 200°F

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

Die FC-Vorwärmung für M270M Gr.345S / M270 Gr.50S Verstehen

Shape-grade 345 MPa (50 ksi) steel for rolled bridge members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 200°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Wo M270M Gr.345S / M270 Gr.50S Eingesetzt Wird

Used as rolled W-shapes and channels in bridge cross-frames, diaphragm members, and built-up sections. The "S" shape designation indicates procurement under AASHTO M270 with shape-specific chemistry and mandatory CVN testing. Common applications include WT sections for cross-frame members, MC channels for diaphragms, and W-shapes for floor beams on shorter spans. Weld details are primarily fillet welds at gusset connections and clip angles.

Wasserstoffkontrolle H4 für M270M Gr.345S / M270 Gr.50S

Shape-grade Gr.345S (50S) benefits from H4 at gusset-to-shape connections where access for torch preheat is limited by flanges and stiffeners. The lower preheat achievable with H4 reduces the thermal management complexity in tight spaces typical of cross-frame subassemblies.

Warum Vorwärmung bei 40–60 mm (1½–2½ in) Wichtig ist

Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.

M270M Gr.345S / M270 Gr.50S bei 40–60 mm (1½–2½ in)

Gr.345S (50S) shapes at 40–65 mm flange thickness are heavy built-up members — typically W14×426 or similar jumbo sections used as pier cap beams or transfer girders. The thick flanges of these shapes require full preheat per the heavy-section tier. Welding on thick rolled sections is complicated by residual stresses from rolling — preheat helps mitigate the cumulative effect of rolling residual stress plus welding shrinkage stress.

H4-Zertifizierte Zusatzwerkstoffe für FC-Brückenschweißen

Die Zusatzbezeichnung H4 zertifiziert, dass der Zusatzwerkstoff höchstens 4 mL diffusiblen Wasserstoff pro 100g abgeschiedenes Schweißgut abgibt. Für bruchkritischen M270M Gr.345S / M270 Gr.50S bei 40–60 mm (1½–2½ in) Dicke mit 1.2–2.0 kJ/mm Wärmeeinbringung erreichen H4-Zusatzwerkstoffe die niedrigste Vorwärmung von 200°F (90°C) in den FC-Tabellen.

Andere Brückenstähle bei H4 1.2–2.0 kJ/mm · 40–60 mm (1½–2½ in)

M270M Gr.345S / M270 Gr.50S bei H4 1.2–2.0 kJ/mm

Verschiedene Kombinationen Ausprobieren

Verwenden Sie den D1.5 Brücken-Vorwärmrechner für jeden AASHTO M270 Stahl, Wasserstoffniveau und Wärmeeinbringungskombination. Siehe auch den D1.1 Vorwärmrechner für Baustahl.